Lupoy® 1302-05
Polycarbonate
LG Chem Ltd.
产品说明:
LUPOY 1302-5 resin is designed for extrusion and injection molding products. It exhibits an excellent physical property balance of heat resistance, transparency and impact strength.
物性信息:
黄卡编号 | E67171-100907363 |
添加剂 | 紫外线稳定剂 |
特性 | 抗撞击性,良好 耐热性,高 清晰度,高 粘度,高 |
用途 | 薄膜 电器用具 镜头 片材 |
UL文件号 | E306922 |
加工方法 | 挤出 注射成型 |
比重 | 1.20 | g/cm³ | ASTM D792 |
熔流率(熔体流动速率) (300°C/1.2 kg) | 5.0 | g/10 min | ASTM D1238 |
收缩率 - 流动 | 0.50 到 0.70 | % | ASTM D955 |
吸水率 | ASTM D570 | ||
23°C, 24 hr | 0.15 | % | ASTM D570 |
平衡, 23°C, 50% RH | 0.32 | % | ASTM D570 |
洛氏硬度 | ASTM D785 | ||
M 级 | 74 | ASTM D785 | |
R 级 | 118 | ASTM D785 |
拉伸模量 | 2480 | MPa | ASTM D638 |
抗张强度 | ASTM D638 | ||
屈服 | 60.0 | MPa | ASTM D638 |
断裂 | 42.0 | MPa | ASTM D638 |
伸长率 | ASTM D638 | ||
屈服 | 6.0 | % | ASTM D638 |
断裂 | 150 | % | ASTM D638 |
弯曲模量 | 2410 | MPa | ASTM D790 |
弯曲强度 | 96.0 | MPa | ASTM D790 |
耐磨耗性 - Change in Haze 1 | 45 | % | ASTM D1004 |
平均燃烧程度 | 3 | cm | ASTM D635 |
悬壁梁缺口冲击强度 2(23°C, 3.20 mm) | 950 | J/m | ASTM D256 |
无缺口悬臂梁冲击 (23°C) | 无断裂 | ASTM D256 | |
装有测量仪表的落镖冲击 3(23°C, 3.20 mm, Total Energy) | 94.0 | J | ASTM D3763 |
载荷下热变形温度 | ASTM D648 | ||
0.45 MPa, 退火, 4.00 mm | 146 | °C | ASTM D648 |
1.8 MPa, 未退火, 4.00 mm | 132 | °C | ASTM D648 |
1.8 MPa, 退火, 4.00 mm | 143 | °C | ASTM D648 |
维卡软化温度 | 151 | °C | ASTM D1525 4 |
球压温度 | > 125 | °C | IEC 60598-1 |
线形热膨胀系数 - 流动 (-40 到 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
体积电阻率 (23°C) | 2.0E+17 | ohms·cm | ASTM D257 |
介电强度 | 17 | kV/mm | ASTM D149 |
介电常数 (60 Hz) | 3.00 | ASTM D150 | |
耗散因数 (60 Hz) | 1.0E-3 | ASTM D150 | |
漏电起痕指数 (2.00 mm) | 250 | V | IEC 60112 |
UL 阻燃等级 | UL 94 | ||
0.500 mm | V-2 | UL 94 | |
1.60 mm | V-2 | UL 94 | |
2.50 mm | V-2 | UL 94 | |
3.00 mm | V-2 | UL 94 | |
热灯丝点火温度 5(2.00 mm) | 850 | °C | IEC 60695-2-13 |
极限氧指数 | 26 | % | ASTM D2863 |
折射率 | 1.586 | ASTM D542 | |
透射率 | 89.0 | % | ASTM D1003 |
雾度 | 0.70 到 1.5 | % | ASTM D1003 |
1 . | 1000g, 500 cycles, CS-10F Wheel |
2 . | 0.25 mm 缺口深度 |
3 . | 3.38 m/sec |
4 . | 速率 A (50°C/h), 载荷2 (50N) |
5 . | 5 sec |
展开全文
其他新闻
- Lupoy® GN2101F 韩国LG 耐热性高,无卤阻燃性 电气/电子应用领域 2024-05-13
- Lupoy® 1201-08 韩国LG 耐热性高,清晰度高,玩具一次性餐具应用 2024-05-13
- Lupoy® GN2101FC 韩国LG 耐热性高,无卤阻燃性,电气/电子应用领域 2024-05-13
- Lumiplas® LD7750 韩国LG 照明漫射器应用料 2024-05-13
- Lupoy® GN1006FM 韩国LG 电气/电子应用领域 2024-05-13
- PA66 H2 G/25-V0KB3/意大利拉题 耐热性、阻燃 2024-05-13
- PA6 6 H2 G/30-V0CT1/意大利拉题 耐热性、阻燃 2024-05-13
- PA6 6 H2 G/30-V0HF1/意大利拉题 磷含量,低(到无)热稳定性 2024-05-13
- PA6 62-03 PD01 G/20/意大利拉题 导电级 2024-05-13
- PA6 63-08 PD02 G/25/意大利拉题 25% 玻璃纤维增强 2024-05-13